Sealing and sealing shall be carried out in the pipeline. The wall thickness of general coiled pipe is 20mm and the outer diameter is 450-3000mm. The production process of general thick walled coiled pipe can be divided into cold drawing and hot rolling directly from the production process of steel plate rolling and general thick walled coiled pipe. The production process of cold-rolled seamless steel pipe is generally more complex than hot rolling. Roll sizing test shall be carried out for the pipe blank first. If there is no response crack on the surface the round pipe shall be cut by cutting machine and cut into a blank with a length of about meters. However, when entering the annealing process, acid shall be used for annealing, and attention shall be paid to whether a large number of bubbles are generated on the surface. If a large number of bubbles are generated, it indicates that the quality of steel pipe can not meet the response standard. In appearance, the cold-rolled seamless steel pipe is shorter than the hot-rolled seamless steel pipe, and its wall thickness is generally smaller than that of the hot-rolled seamless steel pipe, but the surface is brighter than that of the thick wall seamless steel pipe. There is not too much roughness on the surface, and there are not too many burrs in the diameter. The thick wall coiled pipe is a powerful manufacturer, quotation, honest operation, genuine and of the same quality. The thick wall coiled pipe is available from stock, with complete specifications,. Welding, forming, butt joint and pipe rolling, with short processing time, fast delivery and low cost, are mainly used for hot-rolled thick wall coils such as pipes, billboard and columns. The thickness of hot-rolled thick wall coils is generally greater than 20mm and the outer diameter is 450-3000mm. The hot-rolled thick wall coils are rolled under the heating of steel plates Welding, forming, deburring, defect detection and delivery. Sometimes the wall thickness is relatively thick and secondary heating is required. The feature is that the outer diameter tolerance is small Uniform wall thickness. It is important that the hot rolled thick wall coil will not damage the properties of raw materials. The disadvantages of hot roll thick wall rolling pipe are long processing time and. Professional hot-rolled steel pipe, large-diameter thick wall coil, thick wall straight seam coil, steel casing, coil factory inspection is strict, quality assurance. Preferential activities are in progress, welcome to consult. Hot-rolled thick wall coil is widely used: cylinder block, hydraulic pressure, bridge, roller table, etc.
Due to the continuous application of thick wall coiled pipe in industry and the continuous expansion of its scope, it has many advantages. In order to prevent the thick wall coiled pipe from rusting, we can apply antirust oil on the surface of the thick wall coiled pipe.
.The purpose of pipe end sizing is to reduce the ellipticity of thick wall coiled pipe and ensure the dimensional accuracy of thick wall coiled pipe after machining. It is mainly used for oil casing. The number of casing after end sizing is less, and the number of missing threads on the end can improve the yield.
For external welding, a larger welding current is used. However, under the condition of high welding current, the stirring effect of molten pool is enhanced, and the melting amount of welding wire increases accordingly resulting in the increase of weld reinforcement, the deterioration of weld formation and poor edge transition.
.The rolled pipe shall meet the specified arc degree, end face deviation, straightness, etc.
The thickness of thick wall coiled pipe is generally greater than 20mm, and the outer diameter range is 450-3000mm. The thick wall coiled pipe is rolled under the condition of steel plate heating Welding, forming, rib, defect detection, factory. Sometimes the wall thickness is relatively thick and secondary heating is required. The feature is that the outer diameter tolerance is small Uniform wall thickness.
The pipeline installation sequence shall be adopted according to the principle of zoning and subsystem. First the lower level, then the upper level, and then the difficulty. In principle, the pipes connected to the machine are arranged from inside to outside to reduce the impact of welding stress on the installation accuracy of the machine. The joints of indoor and outdoor pipes shall be left outdoors. Q345B thick wall continuous pipe is a widely used carbon steel material. Q345B thick wall continuous pipe with thickness greater than 10mm is widely used in drainage engineering, sewage pipeline, dredging pipeline, construction pipeline, etc. Q345B thick wall continuous pipe is a welded steel pipe product with relatively simple and flexible process. This kind of steel pipe is usually not in stock and is customized. If the quantity is small the raw materials are not good. The main problem of Q345B thick wall continuous pipe is welding. As long as possible, delivery related requirements can be compared with other products.
Meet the following requirements: 1. The longitudinal joint of butt joint shall not be greater than 10% of the wall thickness plus 2mm, and shall not be greater than 3mm. 2. The longitudinal joint of joint 200mm away from the pipe end shall not be greater than 2mm. 3. Other parts shall not be greater than 1mm. 4. The vertical deviation between the end face of coiled pipe and the center line shall not be greater than percent of the outer diameter of pipe and shall not be greater than 3mm. The straightness deviation shall not exceed 1mm / m. 5 the weld cannot be double-sided molded coiled pipe. When the nominal diameter is greater than or equal to 600mm, it is recommended to seal and seal in the pipe. In order to obtain better uniform cleanliness and roughness distribution, which may cause the anti-corrosion layer to become thinner at the peak of the cloud path. At the same time, because the cloud path is too deep bubbles are easy to form in the process, which seriously affects the performance of the layer.
Purpose of steel plate rolling: steel plate rolling is mostly used in large-scale steel structure construction as the main support part, such as bridge piling, seabed piling and high-rise building piling. Its material: Q345C. Q345D and Q345E are also used in low temperature areas.
It is important that the thick wall coiled pipe will not damage the performance of raw materials. The disadvantage of hot roll thick wall rolling pipe is that the treatment time is long Very expensive. Thick wall rolling pipe is widely used: cylinder, hydraulic, bridge, roller, etc.
Inspection requirements.All continuous pipe welds shall be penetration tested.
Welding voltage because the welding arc is conical, and the welding voltage directly affects the length of the arc. Therefore, the general production process of thick wall continuous pipe can be divided into cold drawing and hot rolling. The production process of cold rolled seamless steel pipe is generally more complex than that of hot rolled steel pipe. First, the round pipe will be cut and the growth of the blank is about M. However, during annealing, and attention should be paid to whether there are a large number of bubbles on the surface. If a large number of bubbles appear, the quality of the steel pipe will not meet the response standard. The appearance of cold-rolled seamless steel pipe is shorter than that of hot-rolled seamless steel pipe, and the wall thickness is generally smaller than that of hot-rolled seamless steel pipe, but the surface is brighter than that of thick wall seamless steel pipe, the surface is not too rough, the diameter is not too prickly, and the strength is high. The manufacturer offers, operates in good faith, and has a real price. The same specification thick wall continuous pipe, spot supply,. With the increase of welding voltage, the arc length increases, the moving range of solder joint increases and the molten pool widens. If welding is carried out in a horizontal position, the weld width will be changed, but the edge transition of the weld will not be affected. However, the external welding of spiral welded pipe is carried out on the slope, and the molten weld metal will flow laterally under the action of gravity. We specialize in providing hot-rolled steel pipe, thick wall straight seam continuous pipe, steel casing and quality assurance of pipe rolling plant. During the preferential activities, new and old customers are welcome to consult. Therefore, the greater the welding voltage, the wider the weld pool, the more serious the transverse flow of weld metal, and finally lead to the bias of weld metal.
The convex hull on the surface of the crimp roll shall be treated. Before repeated processing the equipment surface shall be treated to prevent the convex hull steel plate with abnormal roll surface from causing pits.
During pipe rolling, the surface damage of steel plate shall be prevented. The parts with serious scratches must be polished for transition, and the wall thickness of the polished parts shall not be less than the design wall thickness.
The cheapest.This measurement method overcomes the problem of steel
Hot coil thick wall pipe rolling process before hot coil thick wall pipe processing, select an appropriate hot coil machine, and determine whether cold coil, warm coil or hot coil.
High. Hot rolled thick wall coiled pipe is widely used: oil cylinder, hydraulic pressure, roller, etc.
.Pipe groove processing and joint pair: when the pipe wall thickness is less than 6mm, it is type I weld; when the pipe wall thickness is greater than 6mm, it is type V weld; For pipes with diameter greater than 600mm and wall thickness greater than 6mm, the bottom of the pipe shall be sealed at the bottom of the pipe; In addition to the lap joint, the other type of gas coil pipe is continuous and solid V-groove butt welding. If the weld is found to be defective, the weld must be re welded. Rewelding shall not be more than twice. The longitudinal weld of coiled pipe in the same cylindrical part shall not be greater than, and the spacing between two longitudinal joints shall not be less than 200mm.
Steel plate materials mainly include Q235, Q345, 20, 45 35cimo and 42cimo, with 16 manganese and 16 manganese capacity. Generally, cold rolled plate can be used for pipe winding. Like oil, chemicals, natural gas transportation, piling and urban water supply, heating, gas supply and other projects can be customized! The required thickness and length can be adjusted as required! The rolling pipe weld is a double-sided weld. Two longitudinal welds are allowed, and the weld spacing exceeds 300 mm. The welding appearance and quality standard shall not be lower than the level standard in the welding specification.
Generally, the wall thickness of coiled pipe is 20mm and the outer diameter is 450-